Epoxy and Polyester RESINS, HARDENERS AND GELCOATS

Showing 61-72 of 132 item(s)

Hardener C

eshop_001030

Hardener for curing epoxy resin C. Mixing ratio resin:hardener= 100:60 (by weight). Processing time: 50 min. Details can be found in the R+G Handbook p.77/78

Kč812.58

-Kč127.47

Hardener for curing molding resin F 200. The mixing ratio is 100:25 /by weight/. Processing time 100g/25 C 15-20min., gel time 1 mm. 1-2 h., curing at 25 C 24 h. Hardener F 250 is suitable for use in the production of molds without the requirement for thermal curing.

Kč764.84 Kč892.31

Time left

Hardener H 10

eshop_111070

Hardener H 10 is used for curing epoxy systems with increased UV stability* primarily for casting, laminating, coating, and adhesive epoxy systems. Processing can take place at a minimum of 10°C. The advantages of the products are excellent smoothness and good surface

Kč566.61

Hardener H 100 for epoxy spray gelcoat EG 100-W and EG 100-T

eshop_001046

Hardener for epoxy gelcoats. Mixing for EG 100 T: H100= 100:40 and for EG 100 W:H100= 100:26 by weight. Mix the gelcoat and hardener in the prescribed ratio and stir thoroughly. Only then can it be diluted if necessary. Do not load until the coating is fully cured.

Kč1,200.56

Hardener H 10A

eshop_111224

Hardener H 10A is a hardener as a replacement for H10. This hardener is particularly suitable for applications where the requirement is for the clearest possible laminating system. For example, for visible layers made in the first layer from glass fabric with an aluminum surface or in case

Kč659.58

Hardener H 10B

eshop_111227

Hardener in combination with LH 160 and LH 210, ratio 100 to 47. Suitable for encapsulating self-adhesive labels. In a layer of 1-2mm, it provides a bubble-free surface. The surface stops being sticky after about 16-24 hours. Provides a clear, more flexible composite.

Kč581.98

Hardener H 145 (HAVEL)

eshop_111032

Mixing ratio 100:33, working time 50 min. Must be tempered to at least 50°C

Kč579.78

Hardener H 146

eshop_111198

High-quality hardener for curing epoxy resins. The mixing ratio with LH 160, LH 145, and LH 130 is 100:30 by weight, with a processing time of 50-60 min. The minimum curing temperature is 25 °C, but 30 °C and above is recommended.

Kč512.44

Hardener H 147 (HAVEL)

eshop_111030

Top-quality hardener for epoxy resin LH 160 recommended for the production of certified parts not only in aviation. Mixing ratio 100:25, slow hardener with a working time of 90 min. To achieve the parameters for which this hardener is recommended, it is necessary to tem

Kč566.61

Hardener H 206C

eshop_111226

Hardener H 206C is a hardener for casting epoxy resins. It is suitable for preparing clear composites for all types of laminations at temperatures above 15°C. The cured resin is not brittle and does not require conditioning, although higher thermal resistance of the cured resin can be achieved.

Kč722.53

Hardener H 25

eshop_111067

Hardener H 25 was developed as a replacement for P 11. Unlike hardener P 11, no harmful vapors are released during processing, and additionally, the cured epoxy exhibits significantly higher strengths. The hardener is suitable not only as a replacement in epoxy resins from Spolchemi

Kč629.30

Hardener H 282

eshop_112219/1

Cured polyvinyl chloride foam for the production of sandwich structures with higher thermal resistance. Panel size: 2150x1000 mm. Suitable for laminating and bonding with polyester, vinylester, or epoxy. PVC foam coated with glass, aramid, carbon or

Kč433.37

View