Hardeners HAVEL

Showing 1-30 of 30 item(s)

Epodur 619-0600 component B

eshop_001069

Colorless hardener, suitable for casting systems or laminating with a longer processing time: approx. 4 hours.\n\nRiver table. Mixing ratio epoxy:hardener=100:40 by weight. Maximum layer 2cm. Subsequent curing required min. 50°C for 3 hours!

Kč975.09

Hardener H 10

eshop_111070

Hardener H 10 is used for curing epoxy systems with increased UV stability* primarily for casting, laminating, coating, and adhesive epoxy systems. Processing can take place at a minimum of 10°C. The advantages of the products are excellent smoothness and good surface

Kč566.61

Hardener H 10A

eshop_111224

Hardener H 10A is a hardener as a replacement for H10. This hardener is particularly suitable for applications where the requirement is for the clearest possible laminating system. For example, for visible layers made in the first layer from glass fabric with an aluminum surface or in case

Kč659.58

Hardener H 10B

eshop_111227

Hardener in combination with LH 160 and LH 210, ratio 100 to 47. Suitable for encapsulating self-adhesive labels. In a layer of 1-2mm, it provides a bubble-free surface. The surface stops being sticky after about 16-24 hours. Provides a clear, more flexible composite.

Kč581.98

Hardener H 145 (HAVEL)

eshop_111032

Mixing ratio 100:33, working time 50 min. Must be tempered to at least 50°C

Kč579.78

Hardener H 146

eshop_111198

High-quality hardener for curing epoxy resins. The mixing ratio with LH 160, LH 145, and LH 130 is 100:30 by weight, with a processing time of 50-60 min. The minimum curing temperature is 25 °C, but 30 °C and above is recommended.

Kč512.44

Hardener H 147 (HAVEL)

eshop_111030

Top-quality hardener for epoxy resin LH 160 recommended for the production of certified parts not only in aviation. Mixing ratio 100:25, slow hardener with a working time of 90 min. To achieve the parameters for which this hardener is recommended, it is necessary to tem

Kč566.61

Hardener H 206C

eshop_111226

Hardener H 206C is a hardener for casting epoxy resins. It is suitable for preparing clear composites for all types of laminations at temperatures above 15°C. The cured resin is not brittle and does not require conditioning, although higher thermal resistance of the cured resin can be achieved.

Kč722.53

Hardener H 25

eshop_111067

Hardener H 25 was developed as a replacement for P 11. Unlike hardener P 11, no harmful vapors are released during processing, and additionally, the cured epoxy exhibits significantly higher strengths. The hardener is suitable not only as a replacement in epoxy resins from Spolchemi

Kč629.30

Hardener H 282

eshop_112219/1

Cured polyvinyl chloride foam for the production of sandwich structures with higher thermal resistance. Panel size: 2150x1000 mm. Suitable for laminating and bonding with polyester, vinylester, or epoxy. PVC foam coated with glass, aramid, carbon or

Kč433.37

View

-Kč18.97

Hardener H 282 - for LH 288

112219/1

Hardener H 282 is a liquid low-viscosity hardener for epoxy resins. The hardener is based on cyclic diamine. For good orientation, the hardener is colored. Application: Hardener H 282 is a hardener for epoxy resins. It is suitable for all types of laminations during

Kč351.00 Kč369.97

Time left

Hardener H 285 HAVEL

eshop_111260/1

The laminating resin and hardener system was developed as a direct replacement for the well-known LR 285 system from MGS (Hexion). It is suitable for the production of composites using glass, carbon, and aramid fibers and is characterized by high static and dynamic properties.

Kč737.91

Hardener H 286 HAVEL

eshop_111091

Kč702.77

Hardener H 287 HAVEL

eshop_111260

Kč1,057.08

Hardener H 289

eshop_111118/2

Characteristics: it is a liquid hardener for epoxy resins. The hardener is based on cycloaliphatic polyamine. Physical parameters: Viscosity at 25°C 7 - 11 m Pa.s. Hydrogen equivalent 59 g Density at 20 °C 930- 960 kg/m 3 Application: Hardener H 289 is

Kč742.30

Hardener H 300

eshop_111025

Fast hardener with reduced exotherm, high temperature resistance (approx. 90°C) and high flexibility. Used in HAVEL and MGS epoxy resins. We recommend tempering at a minimum of 50°C. Hardening ratio 100:25

Kč934.10

Hardener H 330

eshop_111059

H 330 is suitable for epoxy LH 330, mixing ratio epoxy:hardener = 100:40 by weight or 100:50 by volume. Gel time at 25 degrees Celsius is 70 min. Thermal resistance is 50 degrees Celsius. Viscosity of the mixture at 25 degrees Celsius is 450 mPas/s. The material was developed

Kč547.57

Hardener H 505

eshop_111118

Hardener H 505 is a hardener for epoxy resins. It is suitable for all types of laminations at temperatures above 15°C. Higher thermal resistance of the cured resin can be achieved by post-curing the system at an elevated temperature of 50-60 °C. It belongs to the so-called fast hardeners. Hard

Kč512.44

Hardener H 507

eshop_111206

Characteristics: it is a liquid hardener for epoxy resins. The hardener is based on cycloaliphatic polyamine and does not contain nonylphenol. Physical parameters: Viscosity at 25°C (m Pa.s.) 7 - 11 Hydrogen equivalent g/mol 50 Density at 20 °C kg/m 3 930-

Kč513.90

Hardener H 507 A

eshop_111206/1

Hardener H 507 A is suitable for all types of laminations at temperatures above 15°C. Higher thermal resistance of the cured resin can be achieved by post-curing the system at an elevated temperature of 50-60 °C. Working time is approximately 40 minutes. The low viscosity of the mixture ensures quick

Kč573.93

Hardener H 508

eshop_111205

Characteristics: it is a liquid hardener for epoxy resins. The hardener is based on cycloaliphatic polyamine, the main component is Isophorone diamine. It does not contain nonylphenol. Physical parameters: Viscosity at 25°C (m Pa.s) 7 - 11 Hydrogen equivalent (g/mol)

Kč540.25

Hardener H 509

eshop_111114

Hardener H 509 is a hardener for epoxy resins. It is suitable for all types of laminations at temperatures above 15°C. Higher thermal resistance of the cured resin can be achieved by post-curing the system at an elevated temperature of 50-60 °C. Working time is approximately 70-90 m

Kč600.28

Hardener H 512

eshop_111210

Hardener H 512 is a liquid low-viscosity hardener for epoxy resins. The hardener is based on cyclic diamine. It is suitable for all types of laminations at temperatures above 15°C and where high thermal resistance is required. For proper curing, it is

Kč563.68

Hardener H 513

eshop_111213

Hardener H 513 (Previously H 284) is a hardener for epoxy resins. It is suitable for all types of laminations at temperatures above 15°C and where high thermal resistance is required. Higher thermal resistance of the cured resin can be achieved by post-curing sys

Kč538.06

Hardener H 514

eshop_111245

Hardener H 514 is a liquid low-viscosity hardener for epoxy resins. The hardener is based on cyclic diamine. Hardener H 514 is a hardener for epoxy resins. The working time is in the range of 10-15 minutes. Ratio to resin LH 206AH : H 514

Kč623.41

Hardener H 533

eshop_112228

Hardener H 533 is a liquid mixed hardener containing hydroxylated amine for low molecular weight epoxy resins. Hardener H 533 is characterized by a short processing time of 10-15 min. Hardener H 533 is a hardener for epoxy resins. It is suitable for all

Kč566.61

Hardener H 534

eshop_112229/1

Hardener H 534 is a liquid mixed hardener containing hydroxylated amine for low molecular weight epoxy resins. Hardener H 534 is characterized by a short processing time of 15-25 min. It is suitable for all types of laminations at temperatures above 15°C. Processing time

Kč440.69

Hardener H 535

eshop_111218

Hardener H 535 is a liquid mixed hardener containing hydroxylated amine for low molecular weight epoxy resins. Hardener H 535 is characterized by a short processing time of 25-30 min. Hardener H 535 is a hardener for epoxy resins. It is suitable for all

Kč566.61

Hardener H 536

eshop_111219

Characteristics: Hardener H 536 is a liquid mixed hardener containing hydroxylated amine for low molecular weight epoxy resins. Hardener H 536 is characterized by a longer processing time of 60-80 min. It is suitable for all types of laminations at temperatures

Kč661.04

Hardener H 538

eshop_111243

Hardener H 538 is a hardener for epoxy resins. It is suitable for\nmost laminations at temperatures above 15°C. Working time is 60-80\nmin. The product is not brittle. The composite is recommended to be\ntempered at 50°C for 3 – 5 hours. Higher temperatures

Kč801.16

*Hardeners HAVEL*

Hardeners HAVEL