Epoxy resins, hardeners and gelcoats

Showing 49-72 of 102 item(s)

Hardener 135 (MGS)

eshop_001008/1

Hardener for curing epoxy resin L 135, L 160, L, LR, LR, LR 100, LH 160. The mixing ratio is 100:35/by weight/ or 100:40/by volume/. Processing time for 100g /20 C is 25-30 min. Further necessary information can be obtained at http://www.momentive.com/

Kč819.90

Hardener 136 (MGS)

eshop_001019

Hardener for curing epoxy resin L 135, L 160, L, LR, LR, LR 100, LH 160. The mixing ratio is 100:35/by weight/ or 100:40/by volume/. Processing time for 100g /20 C is 1 - 2 hours. Further necessary information can be obtained at http://www.momentive.com/

Kč948.74

Hardener 285 (MGS)

eshop_001009

Hardener for curing epoxy resin 285. The mixing ratio is 100:40 /by weight/ 100:50 /by volume/ Processing time 100g / 20 C 50 minutes. For more detailed processing instructions see the technical data sheets MGS. Additional necessary information can be obtained at http://www.moment

Kč1,172.74

Hardener 286 (MGS)

eshop_001010

Hardener for curing epoxy resin 285. The mixing ratio is 100:40 /by weight/ 100:50 /by volume/ Working time 100g / 20 C 2 h. For more detailed processing instructions see the tech. sheets MGS. Further necessary information can be obtained at http://www.momentive.c

Kč1,156.27

Hardener 287 (MGS)

eshop_001011

Hardener for curing epoxy resin 285. The mixing ratio is 100:40 /by weight/ 100:50 /by volume/ Processing time 100g / 20 C 4 h. For more detailed processing instructions see the technical data sheets MGS. Further necessary information can be obtained at http://www.momentive.c

Kč1,583.95

-Kč97.83

Hardener 500 MGS

001024

Hardener for curing epoxy resin 285 Mixing ratio is 100:40/by weight and 100:50/by volume/. Working time 100g/20 C is 10-15 min. Hardener for fast curing even at low temperatures from +10 C You can find more necessary information like this

Kč1,043.50 Kč1,141.33

Time left

Hardener 7067 for gelcoat

eshop_900883

Hardener for transparent gelcoat 7060, more information in TL and BL.

Kč1,434.82

Hardener C

eshop_001030

Hardener for curing epoxy resin C. Mixing ratio resin:hardener= 100:60 (by weight). Processing time: 50 min. Details can be found in the R+G Handbook p.77/78

Kč812.58

-Kč127.47

Hardener F 250 /MGS/

001057

Hardener for curing molding resin F 200. The mixing ratio is 100:25 /by weight/. Processing time 100g/25 C 15-20min., gel time 1 mm. 1-2 h., curing at 25 C 24 h. Hardener F 250 is suitable for use in the production of molds without the requirement for thermal curing.

Kč764.84 Kč892.31

Time left

Hardener H 10

eshop_111070

Hardener H 10 is used for curing epoxy systems with increased UV stability* primarily for casting, laminating, coating, and adhesive epoxy systems. Processing can take place at a minimum of 10°C. The advantages of the products are excellent smoothness and good surface

Kč566.61

Hardener H 100 for epoxy spray gelcoat EG 100-W and EG 100-T

eshop_001046

Hardener for epoxy gelcoats. Mixing for EG 100 T: H100= 100:40 and for EG 100 W:H100= 100:26 by weight. Mix the gelcoat and hardener in the prescribed ratio and stir thoroughly. Only then can it be diluted if necessary. Do not load until the coating is fully cured.

Kč1,200.56

Hardener H 10A

eshop_111224

Hardener H 10A is a hardener as a replacement for H10. This hardener is particularly suitable for applications where the requirement is for the clearest possible laminating system. For example, for visible layers made in the first layer from glass fabric with an aluminum surface or in case

Kč659.58

Hardener H 10B

eshop_111227

Hardener in combination with LH 160 and LH 210, ratio 100 to 47. Suitable for encapsulating self-adhesive labels. In a layer of 1-2mm, it provides a bubble-free surface. The surface stops being sticky after about 16-24 hours. Provides a clear, more flexible composite.

Kč581.98

Hardener H 145 (HAVEL)

eshop_111032

Mixing ratio 100:33, working time 50 min. Must be tempered to at least 50°C

Kč579.78

Hardener H 146

eshop_111198

High-quality hardener for curing epoxy resins. The mixing ratio with LH 160, LH 145, and LH 130 is 100:30 by weight, with a processing time of 50-60 min. The minimum curing temperature is 25 °C, but 30 °C and above is recommended.

Kč512.44

Hardener H 147 (HAVEL)

eshop_111030

Top-quality hardener for epoxy resin LH 160 recommended for the production of certified parts not only in aviation. Mixing ratio 100:25, slow hardener with a working time of 90 min. To achieve the parameters for which this hardener is recommended, it is necessary to tem

Kč566.61

Hardener H 206C

eshop_111226

Hardener H 206C is a hardener for casting epoxy resins. It is suitable for preparing clear composites for all types of laminations at temperatures above 15°C. The cured resin is not brittle and does not require conditioning, although higher thermal resistance of the cured resin can be achieved.

Kč722.53

Hardener H 25

eshop_111067

Hardener H 25 was developed as a replacement for P 11. Unlike hardener P 11, no harmful vapors are released during processing, and additionally, the cured epoxy exhibits significantly higher strengths. The hardener is suitable not only as a replacement in epoxy resins from Spolchemi

Kč629.30

Hardener H 282

eshop_112219/1

Cured polyvinyl chloride foam for the production of sandwich structures with higher thermal resistance. Panel size: 2150x1000 mm. Suitable for laminating and bonding with polyester, vinylester, or epoxy. PVC foam coated with glass, aramid, carbon or

Kč433.37

View

-Kč18.97

Hardener H 282 - for LH 288

112219/1

Hardener H 282 is a liquid low-viscosity hardener for epoxy resins. The hardener is based on cyclic diamine. For good orientation, the hardener is colored. Application: Hardener H 282 is a hardener for epoxy resins. It is suitable for all types of laminations during

Kč351.00 Kč369.97

Time left

Hardener H 285 HAVEL

eshop_111260/1

The laminating resin and hardener system was developed as a direct replacement for the well-known LR 285 system from MGS (Hexion). It is suitable for the production of composites using glass, carbon, and aramid fibers and is characterized by high static and dynamic properties.

Kč737.91

Hardener H 286 HAVEL

eshop_111091

Kč702.77

Hardener H 287 HAVEL

eshop_111260

Kč1,057.08

Hardener H 289

eshop_111118/2

Characteristics: it is a liquid hardener for epoxy resins. The hardener is based on cycloaliphatic polyamine. Physical parameters: Viscosity at 25°C 7 - 11 m Pa.s. Hydrogen equivalent 59 g Density at 20 °C 930- 960 kg/m 3 Application: Hardener H 289 is

Kč742.30